Skip to content

Phosphor Peak¶

These two examples, T031_P_Peak_1D and T032_P_Peak_2D show full multicomponent diffusion with coupling to Thermo-Calc™ using industrial steel grades. The first example is one-dimensional and provides a ready benchmark against DICTRA™.

Solidification process at $t=162.0015s$ showing the ferrite/BCC_A2 (orange), austenite/FCC_A1 (white) and liquid (red) as well as the diffuse phase interfaces (blue)

Alloy¶

Example	A015_AlSiMg_Unresolved
Alloy system	Fe-C-Mn-Si-P (Fe_C_Mn_Si_P.Ges5)
Composition	0.4 wt% C 0.8 wt% Mn 0.7 wt% Si 0.03 wt% P
Transition	Solidification

Simulation conditions¶

Example	T031_P_Peak_1D	T032_P_Peak_2D
Dimension	1-D	2-D
Grid size	200 cells	400x400 cells
Grid spacing	0.5 microns	2 microns
Interface thickness	5 cells	4 cells
Boundary conditions	Phase field east = insulation west = insulation bottom = insulation top = insulation Concentration field east = insulation west = insulation bottom = insulation top = insulation	Phase field east = symmetric west = symmetric bottom = periodic top = periodic Concentration field east = periodic west = periodic bottom = periodic top = periodic
Solid phases	BCC_A2 (ferrite) and FCC_A1 (austenite)

Results¶

1-D¶

T031_P_Peak_1D

1-D concentration fields at $t = 2000{\rm s}$ .

C	Mn	P	Si

2-D¶

T032_P_Peak_2D

Solidification sequence

ferrite/BCC_A2 (orange), austenite/FCC_A1 (white), liquid (red), interface (blue)

$t=0s$	$t=50s$	$t=100s$

$t=150s$	$t=160s$	$t=161.0015s$

$t=162.0015s$	$t=166.7638s$	$t=170s$

$t=200s$	$t=500s$	$t=3000s$

Manganese (Mn) concentration evolution

$t=0s$	$t=20s$

$t=700s$	$t=1000s$

Files¶